Originally Posted by rvacha
I am not trying to be a pain, I just want to make sure I understand this correctly. In your 3PC list you have stated that one of the disadvantages was "Spun-forged rim halves" It is not the spun forged/flow formed part you take objection to, it's the halves?
BTW your posts have been a great help and I highly appreciate your efforts!
Thats why I prefer to use the correct terminology. "Spun-Forged" rim halves are sometimes bare aluminum that is flow-formed and has never been forged. People assume that since they have been flow-formed that they are "Forged".